力学性能 | 测试值 | 单位 | 测试标准 | |||||||
拉伸强度 | LW | 230-600 | Mpa | ASTM D-638 | ||||||
CW | 45-80 | |||||||||
拉伸模量 | LW | 18-30 | Gpa | ASTM D-638 | ||||||
CW | 7-13 | |||||||||
弯曲强度 | LW | 300-700 | Mpa | ASTM D-790 | ||||||
CW | 80-120 | |||||||||
弯曲模量 | LW | 20-26 | Gpa | ASTM D-790 | ||||||
CW | 7-12 | |||||||||
压缩强度 | LW | 280 | Mpa | ASTM D-695 | ||||||
CW | 105 | |||||||||
压缩模量 | LW | 21 | Gpa | ASTM D-695 | ||||||
CW | 7.9 | |||||||||
层间剪切强度 | LW | 25 | Mpa | ASTM D-2344 | ||||||
冲击强度 | 280 | KJ/M2 | ASTM D-256 | |||||||
物理性能 | 测试值 | 单位 | 测试标准 | |||||||
巴氏硬度 | 50 | --- | ASTM D-495 | |||||||
吸水率(25℃,24h) | 0.2-0.5 | % | ASTM D-570 | |||||||
密度 | 1.75-2.00 | g/cm3 | ASTM D-792 | |||||||
热膨胀系数(LW) | 5.0 | 10-6/℃ | ASTM D-696 | |||||||
导热系数 | 0.4 | W/(m.K) | ASTM C-518 | |||||||
断裂伸长率 | 0.9 | % | ASTM D-638 | |||||||
电学性能 | 测试值 | 单位 | 测试标准 | |||||||
耐电弧性(LW) | 120 | 秒 | ASTM D-495 | |||||||
介电常数(PF) | 5 | @60hz | ASTM D-150 | |||||||
介电强度(PF) | 8 | KV/mm | ASTM D-149 | |||||||
介电强度(LW) | 1.6 | KV/mm | ASTM D-149 | |||||||
表面电阻系数 | 1015-1012 | Ω | ASTM D-257 | |||||||
体积电阻系数 | 1015-1012 | Ω.cm | ASTM D-257 | |||||||
阻燃性能 | 测试值 | 单位 | 测试标准 | |||||||
隧道试验 | Max 25 | 秒 | ASTM E-4 | |||||||
氧指数 | 25-28 | % | ASTM 2863 | |||||||
28-32 | ||||||||||
>32 | ||||||||||
可燃性分級 | 自熄 | ASTM D635 |
※ LW –纵向 CW-横向 PE=垂直层面